RT journal article
T1 Impregnation of biodegradable polymer using a pressurized soaking method for food packaging
A1 León Marcos, Ludisbel
A1 Montes Herrera, Antonio
A1 García Casas, Ignacio
A1 Valor López, Diego
A1 García Casas, Ignacio
A1 Machado,  Noelia Daiana
A1 Pereyra López, Clara María
A2 Ingeniería Química y Tecnología de Alimentos
K1 Pressurized soaking impregnation
K1 Poly(3-hydroxy-butyrate-co3-hydroxy-valerate)
K1 Biodegradable polymer
K1 Mangifera indica L. leaves
K1 Active food packaging
AB The Pressurized Soaking Impregnation Method combines the main advantages of supercritical solvent impregnation and the soaking casting technique. This work studied the impregnation of poly(3-hydroxy-butyrate-co3-hydroxy-valerate) (PHB-HV) sheets with mango leaf extracts using this method for its future use as active packaging. The influence of temperature (35–55 ºC), pressure (10, 20–30 MPa), and depressurization rate (0.1–5 MPa/min) on the impregnation loads, antioxidant capacities, and mechanical properties of the impregnated samples were evaluated. In addition, the morphological characteristics, colour characterization, and release of active compounds in a food simulant of the PHB-HV samples impregnated at 30 MPa were analysed. The results showed higher impregnation loads (7.66 % wt.) at 30 MPa, 55 ºC, and a slow depressurization rate (0.1 MPa/min). However, the impregnation of antioxidant compounds did not show the expected behaviour, reaching values lower than 3 %. In addition, the samples that were impregnated at 30 MPa showed colour differences that were perceptible to the human eye. A non-homogeneous distribution of impregnation, cracks, and pores on the surface were also observed. The release study in the D1 food simulant showed good agreement with the Peleg model and a quasi-Fickian diffusion behaviour according to the Korsmeyer-Peppas model. The contact time study in the impregnation at 30 MPa, 35 ºC and 0.1 MPa/min revealed a slight increase in antioxidant capacity after six hours. Furthermore, samples with a more homogeneous colour distribution were obtained.
PB Elsevier
SN 2212-9820
YR 2024
FD 2024
LK http://hdl.handle.net/10498/35639
UL http://hdl.handle.net/10498/35639
LA eng
DS Repositorio Institucional de la Universidad de Cádiz
RD 21-sep-2026